DLP 3D 프린팅으로 제작된 고순도 알루미나 세라믹 탈지 공정 연구
A Study on the Debinding Process of High Purity Alumina Ceramic Fabricated by DLP 3D Printing
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The 3D printing process provides a higher degree of freedom when designing ceramic parts than the conventional press forming process. However, the generation and growth of the microcracks induced during heat treatment is thought to be due to the occurrence of local tensile stress caused by the thermal decomposition of the binder inside the green body. In this study, an alumina columnar specimen, which is a representative ceramic material, is fabricated using the digital light process (DLP) 3D printing method. DTG analysis is performed to investigate the cause of the occurrence of microcracks by analyzing the debinding process in which microcracks are mainly generated. HDDA of epoxy acrylates, which is the main binder, rapidly debinded in the range of 200 to 500oC, and microcracks are observed because of real-time microscopic image observation. For mitigating the rapid debinding process of HDDA, other types of acrylates PETA, PUA, and MMA are added, and the effect of these additives on the debinding rate is investigated. By analyzing the DTG in the 25 to 300oC region, it is confirmed that the PETA monomer and the PUA monomer can suppress the rapid decomposition rate of HDDA in this temperature range.
Abstract
The 3D printing process provides a higher degree of freedom when designing ceramic parts than the conventional press forming process. However, the generation and growth of the microcracks induced during heat treatment is thought to be due to the occurrence of local tensile stress caused by the thermal decomposition of the binder inside the green body. In this study, an alumina columnar specimen, which is a representative ceramic material, is fabricated using the digital light process (DLP) 3D printing method. DTG analysis is performed to investigate the cause of the occurrence of microcracks by analyzing the debinding process in which microcracks are mainly generated. HDDA of epoxy acrylates, which is the main binder, rapidly debinded in the range of 200 to 500oC, and microcracks are observed because of real-time microscopic image observation. For mitigating the rapid debinding process of HDDA, other types of acrylates PETA, PUA, and MMA are added, and the effect of these additives on the debinding rate is investigated. By analyzing the DTG in the 25 to 300oC region, it is confirmed that the PETA monomer and the PUA monomer can suppress the rapid decomposition rate of HDDA in this temperature range.
참고문헌 (11)
- Z. Chen, , J. Eur. Ceram. Soc, 39, pp.661~ (2019)
- T. D. Ngo, , Compos. B. Eng, 143, pp.172~ (2018)
- M. Krkobabić, , Int. J. Pharm, 572, pp.118790~ (2019)
- C. Hinczewski, , J. Eur. Ceram. Soc, 18, pp.583~ (1998)
- S. P. Gentry, , J. Eur. Ceram. Soc, 35, pp.1895~ (2015)
- 이현빈, "DLP 기반 3D 프린팅으로 제조된 Al2O3 절삭공구의 기계적 물성 연구", 한국분말재료학회지, 26(6), pp.508~514 (2019), 한국분말재료학회[DOI]
- E. Johansson, , Materials, 10, pp.138~ (2017)
- C. J. Bea, , Int. J. Appl. Ceram. Technol, 8, pp.1255~ (2011)
- 김성현, "광경화성 아크릴 수지의 경화특성에 관한 연구", 폴리머, 34(5), pp.469~473 (2010), 한국고분자학회
- F. Mohtadizadeh, , Prog. Org. Coat, 89, pp.231~ (2015)
- 배창준, "Ceramic Stereolithography: Additive Manufacturing for 3D Complex Ceramic Structures", 한국세라믹학회지, 54(6), pp.470~477 (2017), 한국세라믹학회