Hexagonal-Boron Nitride 강화 시멘트 복합체의 압축강도 향상에 대한 실험적 연구
Experimental Study on Improving Compressive Strength of Hexagonal Boron Nitride Reinforced Cement Composite
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The mechanical properties and microstructures of hexagonal boron nitride (h-BN)-reinforced cement composites are experimentally studied for three and seven curing days. Various sizes (5, 10, and 18 μm) and concentrations (0.1%, 0.25%, 0.5%, and 1.0%) of h-BN are dispersed by the tip ultrasonication method in water and incorporated into the cement composite. The compressive strength of the h-BN reinforced cements increases by 40.9%, when 0.5 wt% of 18 μm-sized h-BN is added. However, the compressive strength decreases when the 1.0 wt% cement composite is added, owing to the aggregation of the h-BNs in the cement composite. The microstructural characterization of the h-BN-reinforced cement composite indicates that the h-BNs act as bridges connecting the cracks, resulting in improved mechanical properties for the reinforced cement composite.
Abstract
The mechanical properties and microstructures of hexagonal boron nitride (h-BN)-reinforced cement composites are experimentally studied for three and seven curing days. Various sizes (5, 10, and 18 μm) and concentrations (0.1%, 0.25%, 0.5%, and 1.0%) of h-BN are dispersed by the tip ultrasonication method in water and incorporated into the cement composite. The compressive strength of the h-BN reinforced cements increases by 40.9%, when 0.5 wt% of 18 μm-sized h-BN is added. However, the compressive strength decreases when the 1.0 wt% cement composite is added, owing to the aggregation of the h-BNs in the cement composite. The microstructural characterization of the h-BN-reinforced cement composite indicates that the h-BNs act as bridges connecting the cracks, resulting in improved mechanical properties for the reinforced cement composite.
참고문헌 (24)
- L. P. Singh, , Constr. Build. Mater, 194, pp.205~ (2019)
- Z. Xu, , Constr. Build. Mater, 125, pp.1169~ (2016)
- F. Sanchez, , Constr. Build. Mater, 24, pp.2060~ (2010)
- L. P. Singh, , C em. Concr. Compos, 79, pp.106~ (2017)
- T. Meng, , Constr. Build. Mater, 29, pp.241~ (2012)
- F. Babak, , Hindawi, 2014, pp.1~ (2014)
- K. Gong, , J. Mater. Civ. Eng, 27, pp.A4014010~ (2015)
- S. Sharma, , Rsc Adv, 5, pp.52642~ (2015)
- J. Fan, , Nanoscale, 4, pp.7046~ (2012)
- S. Chuah, , Constr. Build. Mater, 73, pp.113~ (2014)
- S. M. Kim, , Nat. Commun, 6, pp.8862~ (2015)
- T. S. Qureshi, , Constr. Build. Mater, 206, pp.71~ (2019)
- H. Zhou, , Nano Res, 7, pp.1232~ (2014)
- J. U. Lee, , Phys. Rev. B, 83, pp.081419~ (2011)
- J. Chen, , JEPT Lett, 112, pp.117~ (2020)
- T. Schwamb, , Nanotechnology, 20, pp.40~ (2009)
- V. Vijayaraghavan, , Nanomaterials, 8, pp.546~ (2018)
- P. Beiss, , Springer Materials, 2A2, pp.118~ (2002)
- M. A. Rafiee, , Adv. Funct. Mater, 23, pp.5624~ (2013)
- W. Wang, , Nanoscale, 10, pp.1004~ (2018)
- G. R. Bhimanapati, , Nanoscale, 6, pp.11671~ (2014)
- H. Park, , Sci. Rep, 7, pp.40091~ (2017)
- G. R. Bhimanapati, , Nanoscale, 6, pp.11671~ (2014)
- Y. Xu, , Green Chem, 21, pp.6746~ (2019)