분말성형법으로 제조된 Ag-SnO2-Bi2O3 접점소재의 미세조직 및 특성
Microstructure and Characteristics of Ag-SnO2-Bi2O3 Contact Materials by Powder Compaction
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
In this study, we report the microstructure and characteristics of Ag-SnO2-Bi2O3 contact materials using a controlled milling process with a subsequent compaction process. Using magnetic pulsed compaction (MPC), the milled Ag-SnO2-Bi2O3 powders have been consolidated into bulk samples. The effects of the compaction conditions on the microstructure and characteristics have been investigated in detail. The nanoscale SnO2 phase and microscale Bi2O3 phase are well-distributed homogeneously in the Ag matrix after the consolidation process. The successful consolidation of Ag-SnO2-Bi2O3 contact materials was achieved by an MPC process with subsequent atmospheric sintering, after which the hardness and electrical conductivity of the Ag-SnO2-Bi2O3 contact materials were found to be 62–75 HV and 52–63% IACS, respectively, which is related to the interfacial stability between the Ag matrix, the SnO2 phase, and the Bi2O3 phase.
Abstract
In this study, we report the microstructure and characteristics of Ag-SnO2-Bi2O3 contact materials using a controlled milling process with a subsequent compaction process. Using magnetic pulsed compaction (MPC), the milled Ag-SnO2-Bi2O3 powders have been consolidated into bulk samples. The effects of the compaction conditions on the microstructure and characteristics have been investigated in detail. The nanoscale SnO2 phase and microscale Bi2O3 phase are well-distributed homogeneously in the Ag matrix after the consolidation process. The successful consolidation of Ag-SnO2-Bi2O3 contact materials was achieved by an MPC process with subsequent atmospheric sintering, after which the hardness and electrical conductivity of the Ag-SnO2-Bi2O3 contact materials were found to be 62–75 HV and 52–63% IACS, respectively, which is related to the interfacial stability between the Ag matrix, the SnO2 phase, and the Bi2O3 phase.
참고문헌 (12)
- 권기봉, "Ag-CdO계 전기접점재료의 미세조직에 미치는 열처리 조건과 산화 공정의 영향", 한국주조공학회지, 25(6), pp.226~232 (2005), 한국주조공학회
- J. Chen, , J. Mater. Sci. Technol, 26, pp.49~ (2010)
- Q. Ye, , Mater. Sci. Eng. A, 449-451, pp.1045~ (2007)
- M. Lungu, , J. Optoelectron. Adv. Mater, 8, pp.576~ (2006)
- C. P. Wu, , J. Alloys Compd, 457, pp.565~ (2008)
- P. B. Joshia, , Mater. Lett, 33, pp.137~ (1997)
- C. Xu, , Mater. Sci. Eng. A, 538, pp.202~ (2012)
- G. Li, , Ceram. Int, 46, pp.4897~ (2020)
- G. Schimmel, , Acta. Mater, 58, pp.2091~ (2010)
- 강래철, "자기펄스 가압성형법에 의한 알루미나 나노분말의 치밀화 및 특성 평가", 한국분말재료학회지, 15(1), pp.37~45 (2008), 한국분말재료학회
- J. G. Lee, , Mater. Lett, 64, pp.35~ (2010)
- 김정곤, "친환경 Ag-SnO2 전기접점재료의 분말야금 공정 최적화", 한국분말재료학회지, 14(5), pp.327~332 (2007), 한국분말재료학회