PVA 용액법과 국산 산화알루미늄을 적용하여 대기 플라즈마 용사법으로 합성된 구형의 YAG:Ce3+ 형광체의 발광특성
Optical Properties of Spherical YAG:Ce3+ Phosphor Powders Synthesized by Atmospheric Plasma Spraying Method Appling PVA Solution Route and Domestic Aluminium Oxide Seed
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
YAG phosphor powders were fabricated by the atmospheric plasma spraying method with the spray-dried spherical YAG precursor. The YAG precursor slurry for the spray drying process was prepared by the PVA solution chemical processing utilizing a domestic easy-sintered aluminum oxide (Al2O3) powder as a seed. The homogenous and viscous slurry resulted in dense granules, not hollow or porous particles. The synthesized phosphor powders demonstrated a stable YAG phase, and excellent fluorescence properties of approximately 115% compared with commercial YAG:Ce3+ powder. The microstructure of the phosphor powder had a perfect spherical shape and an average particle s ize of a pprox imately 30 μm. As a r esult of t he PKG t est of t he YAG p hosphor p owder, t he s ynthesized phosphor powders exhibited an outstanding luminous intensity, and a peak wavelength was observed at 531 nm.
Abstract
YAG phosphor powders were fabricated by the atmospheric plasma spraying method with the spray-dried spherical YAG precursor. The YAG precursor slurry for the spray drying process was prepared by the PVA solution chemical processing utilizing a domestic easy-sintered aluminum oxide (Al2O3) powder as a seed. The homogenous and viscous slurry resulted in dense granules, not hollow or porous particles. The synthesized phosphor powders demonstrated a stable YAG phase, and excellent fluorescence properties of approximately 115% compared with commercial YAG:Ce3+ powder. The microstructure of the phosphor powder had a perfect spherical shape and an average particle s ize of a pprox imately 30 μm. As a r esult of t he PKG t est of t he YAG p hosphor p owder, t he s ynthesized phosphor powders exhibited an outstanding luminous intensity, and a peak wavelength was observed at 531 nm.
참고문헌 (16)
- Y. Pan, , Mater. Sci. Eng. B, 106, pp.251~ (2004)
- 정현기, "기계화학적 고상반응에 의한 YAG 분말의 합성 및상 형성 거동에 관한 연구", 한국분말재료학회지, 13(4), pp.243~249 (2006), 한국분말재료학회
- X. Li, , Mater, Res. Bull, 39, pp.1923~ (2004)
- J. Zhou, , J. Luminescence, 119-120, pp.237~ (2006)
- K. M. Kinsman, , J. Am. Ceram. Soc, 77, pp.2866~ (1994)
- Y. C. Kang, , J. Phy. Chem. Solids, 60, pp.185~ (1999)
- Y. C. Kang, , Adv. Mater, 12, pp.451~ (2000)
- E. J. Kim, , Mater. Res. Bull, 38, pp.515~ (2003)
- S. H. Lee, , J. Alloys Compd, 447, pp.776~ (2009)
- M. C. Maniquiz, , J. Electrochem. Soc, 157, pp.H1135~ (2010)
- Z. Y. Liu, , 12th International Conference on Electronic Packaging Technology and High Density Packing (2011)
- 김용현, "폴리머용액법 및 알루미나 seed를 도입한 YAG:Ce3+ 형광체 분말 합성", 한국분말재료학회지, 20(1), pp.37~42 (2013), 한국분말재료학회
- 김아름, "PVA 중합도가 고상-액상 혼합 방식에 의한 YAG:Ce 3+ 형광체분말 합성에 미치는 영향", 한국세라믹학회지, 51(5), pp.424~429 (2014), 한국세라믹학회[DOI]
- S. K. No, , Polym. Sci. Technol, 15, pp.4~ (2004)
- P. Fauchais, , J. Phys. D:Appl. Phys, 37, pp.R86~ (2004)
- H. Zhang, , J. Surf. Coat. Technol, 258, pp.495~ (2014)