고엔트로피합금 분말야금재와 알루미늄 주조재 사이의 계면 반응 연구
Interfacial Reaction between Spark Plasma Sintered High-entropy Alloys and Cast Aluminum
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
This study investigates the interfacial reaction between powder-metallurgy high-entropy alloys (HEAs) and cast aluminum. HEA pellets are produced by the spark plasma sintering of Al0.5CoCrCu0.5FeNi HEA powder. These sintered pellets are then placed in molten Al, and the phases formed at the interface between the HEA pellets and cast Al are analyzed. First, Kirkendall voids are observed due to the difference in the diffusion rates between the liquid Al and solid HEA phases. In addition, although Co, Fe, and Ni atoms, which have low mixing enthalpies with Al, diffuse toward Al, Cu atoms, which have a high mixing enthalpy with Al, tend to form Al–Cu intermetallic compounds. These results provide guidelines for designing Al matrix composites containing high-entropy phases.
Abstract
This study investigates the interfacial reaction between powder-metallurgy high-entropy alloys (HEAs) and cast aluminum. HEA pellets are produced by the spark plasma sintering of Al0.5CoCrCu0.5FeNi HEA powder. These sintered pellets are then placed in molten Al, and the phases formed at the interface between the HEA pellets and cast Al are analyzed. First, Kirkendall voids are observed due to the difference in the diffusion rates between the liquid Al and solid HEA phases. In addition, although Co, Fe, and Ni atoms, which have low mixing enthalpies with Al, diffuse toward Al, Cu atoms, which have a high mixing enthalpy with Al, tend to form Al–Cu intermetallic compounds. These results provide guidelines for designing Al matrix composites containing high-entropy phases.
참고문헌 (19)
- E. A. Starke Jr, , Prog. Aerosp. Sci, 32, pp.131~ (1996)
- M. S. Kim, , Arch. Metall. Mater, 66, pp.3~ (2021)
- H. M. Hu, , Mater. Sci. Eng. A, 297, pp.94~ (2001)
- J. Hirsch, , Acta Mater, 61, pp.818~ (2013)
- L. Kloc, , Metall. Mater. Trans. A, 27, pp.3871~ (1996)
- E. A. Starke, , Prog. Aerosp. Sci, 32, pp.131~ (1996)
- F. Czerwinski, , Adv. Mater. Process, 174, pp.16~ (2016)
- S. M. Shin, , Metals, 9, pp.1108~ (2019)
- L. Y. Chen, , Nature, 528, pp.539~ (2015)
- B. Schuh, , Acta Mater, 96, pp.1~ (2015)
- Y. Liu, , J. Alloy. Compd, 780, pp.558~ (2019)
- Z. Yuan, , J. Alloy. Compd, 806, pp.901~ (2019)
- C. Y. Hsu, , Wear, 268, pp.5~ (2010)
- 박천웅, "Ni5Y 합금상이 형성된 Ni계 산화물 분산강화 아토마이징 분말의 밀링 거동 분석", 한국분말재료학회지, 26(2), pp.101~106 (2019), 한국분말재료학회[DOI]
- A. Takeuchi, , Mater. Trans, 41, pp.11~ (2000)
- S. W. Chee, , Nat. Commun, 10, pp.2831~ (2019)
- A. D. Smigelskas, , Trans. AIME, 171, pp.130~ (1947)
- J. L. Murray, , Int. Met. Rev, 30, pp.211~ (1985)
- K. D. Kim, , Scr. Mater, 159, pp.99~ (2019)