오스테나이트계 316L 스테인리스강의 강도 및 감쇠능에 미치는 미세조직의 영향

Abstract

The effects of microstructure on the damping capacity and tensile properties of 316L stainless steel were investigated. Increasing the degree of cold working, the volume fraction of ε-martensite decreased after rising to maximum value at specific level of cold working, the volume fraction of α'-martensite slowly increased and then dramatically increased from the point of decreasing ε-martensite volume fraction. Increasing the degree of cold working, the behavior of damping capacity is similar to that of the ε-martensite. After the damping capacity showing the maximum value at about 20% of cold rolling, damping capacity was decreased with the volume fraction of ε-martensite. Tensile strength was proportional to the volume fraction of α'-martensite, and elongation steeply decreased in the range low volume fraction of α'-martensite, then slowly decreased in range the above 10% volume fraction of α'-martensite. The damping capacity and elongation is strongly controlled by the volume fraction of ε martensite with liner relationship. However, the effect of the volume fraction of α'-martensite and austenite phase on the damping capacity was not observed. Tensile strength was governed by the volume fraction of α'-martensite.1. 서 론316L스테인리스강은 탄소양이 극히 낮고 2% 이상의 Mo가 첨가되어 있기 때문에 우수한 내식성 외에 강도가 높은 특성을 지니고 있다. 따라서 해양구조물과 선박관련 부품에서부터 항공기 및 화학플랜트 등에 이르기까지 다양하게 이용되고 있다(Stickler and Vinckier, 1961)또한 이 강은 상온에서 준안정 오스테나이트 조직으로 이루어져 있기 때문에 상온 부근의 온도에서 가공 하면 오스테나이트(γ) 조직의 일부가 마르텐사이트 조직으로 변태(가공 유기변태) 하고, 가공에 의해 변태 되는 정도는 오스테나이트 상의 안정도, 가공양 등에 따라 달라지며(Kang and Sung, 1991). 이러한 변태유기 소성 거동은 기계적 성질 뿐만 아니라 진동감쇠능에도 큰 영향을 미치게 될 것이다(Okada et al., 2004).