MoSi2 복합재료의 특성
Properties of MoSi2 Based Composite Materials
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The mechanical properties of MoSi2 based composites containing various types of reinforcement, such as SiC, ZrO2, and W, were investigated, based on detailed examinations of their microstructures. MoSi2 based composites were fabricated at a temperature of 1350℃ using a hot-press device. The volume fraction of SiC and ZrO2 particles in this composite system was fixed as 20%. The volume fraction of three types of W particles was changed from 10% to 30%. The characteristics of the MoSi2 based composites were determined by means of optical microscopy and a three-point bending test. The addition of W particles to the MoSi2 powders exhibited a sufficient improvement in the microstructure and mechanical property of the sintered MoSi2 materials, compared to those of SiC and ZrO2 particles. In particular, W/MoSi2 composites containing W particles of 20 vol% represented a good flexural strength of about 530MPa at room temperature, accompanying a relative density of about 92%. The flexural strength of the W/MoSi2 composites tended to decrease with an increase in the average size of the W particles.
Abstract
The mechanical properties of MoSi2 based composites containing various types of reinforcement, such as SiC, ZrO2, and W, were investigated, based on detailed examinations of their microstructures. MoSi2 based composites were fabricated at a temperature of 1350℃ using a hot-press device. The volume fraction of SiC and ZrO2 particles in this composite system was fixed as 20%. The volume fraction of three types of W particles was changed from 10% to 30%. The characteristics of the MoSi2 based composites were determined by means of optical microscopy and a three-point bending test. The addition of W particles to the MoSi2 powders exhibited a sufficient improvement in the microstructure and mechanical property of the sintered MoSi2 materials, compared to those of SiC and ZrO2 particles. In particular, W/MoSi2 composites containing W particles of 20 vol% represented a good flexural strength of about 530MPa at room temperature, accompanying a relative density of about 92%. The flexural strength of the W/MoSi2 composites tended to decrease with an increase in the average size of the W particles.
참고문헌 (13)
- 노상훈, "Y3Al5O12 첨가가 질화규소 세라믹스의 제조 및 그 기계적 특성에 미치는 영향", 한국해양공학회지, 21(6), pp.95~100 (2007), 한국해양공학회
- 윤한기, "고온선박엔진용 MoSi2 금속간화합물의 경도와 방전가공특성", 한국해양공학회지, 16(6), pp.60~64 (2002), 한국해양공학회
- 이상필, "Al2O3와 Y2O3 입자를 함유한 액상소결 SiC 재료의 특성", 한국해양공학회지, 22(4), pp.59~64 (2008), 한국해양공학회
- Bose, S., "Engineering Aspect of Creep Deformation of Molybdenum Disilicide", Mater. Sci. and Eng., A155, pp.217~225 (1992)
- Carter, D.H., "SiC-MoSi2 Composites", Ceram. Eng. Sci. Proc., 10, pp.1121~1129 (1989)
- Chou, T.C., "Pesting of the Hightemperature MoSi2 Intermetallic", J. Metal., 45, pp.15~21 (1993)
- Courtright, E.L., "A Comparison of MoSi2 Materix Composites with Other Silicon-base Composite Systems", Mater. Sci. and Eng., A261, pp.53~63 (1999)
- Lee, S.P., "Effect of Fabrcating Conditions on Impact Properties of Nb", MoSi2 Laminate Composites, 1998, pp.63, 351~357
- Pan, J., "Fabrication and Characterization of SiC", MoSi2 Composites, 1998, pp.A244, 191~198
- Petrovic, J.J., "Key Developments in High Temperature Structural Silicides", Mater. Sci. and Eng., A261, pp.1~5 (1999)
- Shah, D.M., "Appraisal of Other Silicides as Structural Materials", Mater. Sci. and Eng., A155, pp.45~57 (1992)
- Shaw, L., "Toughening MoSi2 with Niobium Metal-effects of Morphology of Ductile Reinforcements", J. Mater. Sci., 30, pp.849~854 (1995)
- Yang, J.M., "Chemical Compatibility of High Temperature Intermetallic Compounds with Various Potential Reinforcements", Mater. Res. Soc. Sympo., 통권 : 194, pp.385~392 (1990)