라디오파 마그네트론 스퍼터링으로 성장한 질소와 알루미늄 도핑된 ZnO 박막의 특성
Properties of Nitrogen and Aluminum Codoped ZnO Thin Films Grown by Radio-frequency Magnetron Sputtering
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Nitrogen and aluminum codoped ZnO (NAZO) thin films were grown on glass substrates with changing the nitrogen flow ratio by radio-frequency magnetron sputtering. The structural, optical, and electrical properties of the NAZO films were investigated. The surface morphologies and the structural properties of the thin films were analyzed by using the X-ray diffraction and scanning electron microscopy. The NAZO thin film, deposited at nitrogen flow ratio of 0%, showed a strongly c-axis preferred orientation and the lowest resistivity of 3.20-3 Wcm. The intensity of ZnO (002) diffraction peak was decreased gradually with increasing the nitrogen flow ratio. The optical properties of the films were measured by UV-VIS spectrophotometer and the optical transmittances for all the samples were found to be an average 90% in the visible range. Based on the transmittance value, the optical bandgap energy for the NAZO thin film deposited at nitrogen flow ratio of 0% was determined to be 3.46 eV. As for the electrical properties, the carrier concentration and the hall mobility were decreased, but the electrical resistivity was increased as the nitrogen flow ratio was increased.
Abstract
Nitrogen and aluminum codoped ZnO (NAZO) thin films were grown on glass substrates with changing the nitrogen flow ratio by radio-frequency magnetron sputtering. The structural, optical, and electrical properties of the NAZO films were investigated. The surface morphologies and the structural properties of the thin films were analyzed by using the X-ray diffraction and scanning electron microscopy. The NAZO thin film, deposited at nitrogen flow ratio of 0%, showed a strongly c-axis preferred orientation and the lowest resistivity of 3.20-3 Wcm. The intensity of ZnO (002) diffraction peak was decreased gradually with increasing the nitrogen flow ratio. The optical properties of the films were measured by UV-VIS spectrophotometer and the optical transmittances for all the samples were found to be an average 90% in the visible range. Based on the transmittance value, the optical bandgap energy for the NAZO thin film deposited at nitrogen flow ratio of 0% was determined to be 3.46 eV. As for the electrical properties, the carrier concentration and the hall mobility were decreased, but the electrical resistivity was increased as the nitrogen flow ratio was increased.
참고문헌 (15)
- M. L. Tu, , J. Appl. Phys, 100 (2006)
- H. S. Kang, , Appl. Phys. Lett, 88 (2006)
- A. V. Singh, , J. Appl. Phys, 95, pp.3640~ (2004)
- 박이섭, "DC마그네트론 스퍼터링에 의해 증착한 AZO박막의 특성", 한국표면공학회지, 40(3), pp.107~112 (2007), 한국표면공학회
- 이성훈, "ZnO 박막의 전기적 구조적 특성에 미치는 수소유량비의 영향", 한국표면공학회지, 39(6), pp.250~254 (2006), 한국표면공학회
- Shinho Cho, "Structural and Optical Properties of ZnO Films Grown on Sapphire Substrates Subjected to Substrate Temperature", Journal of the Korean Physical Society, 49(3), pp.985~988 (2006), 한국물리학회
- S. T. Tan, , J. Appl. Phys, 98 (2005)
- D. C. Look, , Appl. Phys. Lett, 81, pp.1830~ (2002)
- 황동현, "Al 도핑된 ZnO 박막에서 방출되는 보라색 발광 스펙트럼", 전기전자재료학회논문지, 20(4), pp.318~324 (2007), 한국전기전자재료학회
- Y. J. Zeng, , Appl. Surf. Sci, 249, pp.203~ (2005)
- K. Prabakar, , Cryst. Res. Technol, 40, pp.1150~ (2005)
- H. L. Porter, , J. Appl. Phys, 100 (2006)
- C. Zhang, , Solid State Comm, 132, pp.75~ (2004)
- 조신호, "산소 유량비 변화에 따른 Al 도핑된 ZnO 박막의 구조 및 광학적 특성", 한국진공학회지, 16(4), pp.267~272 (2007), 한국진공학회
- F. Yakuphanoglu, , Opt. Comm, 239, pp.275~ (2004)