전자빔 증발법 박막 증착을 이용한 양극 산화 알루미늄 템플릿의 나노 포어 가공 연구
Study on the narrowed nanopores of anodized aluminum oxide template by thin-film deposition using e-beam evaporation
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The fabrication of nanopore membrane by deposition of Al2O3 film using electron-beam evaporation, which is fast, cost-effective, and negligible dependency on substance material, is investigated for potential applications in water purification and sensors. The decreased nanopore diameter owing to increased wall thickness is observed when Al2O3 film is deposited on anodic aluminum oxide membrane at higher deposition rate, although the evaporation process is generally known to induce a directional film deposition leading to the negligible change of pore diameter and wall thickness. This behavior can be attributed to the collision of evaporated Al2O3 particles by the decreased mean free path at higher deposition rate condition, resulting in the accumulation of Al2O3 materials on both the surface and the edge of the wall. The reduction of nanopore diameter by Al2O3 film deposition can be applied to the nanopore membrane fabrication with sub-100 nm pore diameter.
Abstract
The fabrication of nanopore membrane by deposition of Al2O3 film using electron-beam evaporation, which is fast, cost-effective, and negligible dependency on substance material, is investigated for potential applications in water purification and sensors. The decreased nanopore diameter owing to increased wall thickness is observed when Al2O3 film is deposited on anodic aluminum oxide membrane at higher deposition rate, although the evaporation process is generally known to induce a directional film deposition leading to the negligible change of pore diameter and wall thickness. This behavior can be attributed to the collision of evaporated Al2O3 particles by the decreased mean free path at higher deposition rate condition, resulting in the accumulation of Al2O3 materials on both the surface and the edge of the wall. The reduction of nanopore diameter by Al2O3 film deposition can be applied to the nanopore membrane fabrication with sub-100 nm pore diameter.
참고문헌 (15)
- C. Dekker, , Nat. Nanotechnol, 2, pp.209~215 (2007)
- M. Ulbricht, , Polymer, 47, pp.2217~2262 (2006)
- C. -M. Wang, , Front. Mater. Sci, 7, pp.335~349 (2013)
- 김청, "AAO (Anodized Aluminium Oxide) template 제조 및 이를 이용해 제조한 탄소 및 산화 금속 나노 섬유 물질에 관한 연구", 한국표면공학회지, 49(4), pp.357~362 (2016), 한국표면공학회[DOI]
- Y. Wang, , Sci. Rep, 8, pp.1234~ (2018)
- 유현석, "Layer-by-layer 기법을 통한 Cu2(btc)3-AAO 하이브리드 분리막의 제조", 한국표면공학회지, 51(1), pp.21~26 (2018), 한국표면공학회[DOI]
- L. -J. Cheng, , Chem. Soc. Rev, 39, pp.923~938 (2010)
- R. Torre, , Nanotechnology, 23, pp.385308~ (2012)
- Z. Siwy, , Nucl. Instrum. Methods Phys. Res., B, 208, pp.143~148 (2003)
- T. A. Rebbecchi Jr., , J. Mater. Res, 33, pp.2~15 (2018)
- T. Deng, , Sci. Bull, 60, pp.304~319 (2015)
- S. -W. Nam, , Nano Lett, 10, pp.3324~3329 (2010)
- J. S. Yoon, , Appl. Phys. Lett, 104, pp.901603~ (2014)
- Q. Liu, , Int. J. Mol. Sci, 15, pp.12714~12730 (2014)
- G. Wang, , Res. Chem. Intermed, 43, pp.1447~1463 (2017)