수열합성법에 의한 정렬된 ZnO 나노로드 구조의 합성
Synthesis of Aligned ZnO Nanorod Arrays via Hydrothermal Route
3
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
The nano-array of the vertically aligned rod-like particles grown on ZnO coated glass-substrates was obtained via hydrothermal process. ZnO thin film coatings were prepared on the glass substrates using a MOD (metallorganic deposition) dip-coating method with zinc chloride dihydrate as starting material and 2-ethylhexanol as solvent. ZnO nanorods were synthesized on the seeded substrates by hydrothermal method at 80°C using zinc-nitrate hexahydrate as a Zn source and sodium hydroxide as a mineralizer. Under the hydrothermal condition, the rod-like nanocrystals were easily attaching on the already ZnO seeded (coated) glass surface. It has been shown that the hydrothermal synthesis parameters are key factors in the nucleation and growth of ZnO crystallites. By controlling of hydrothermal parameters, the ZnO particulate morphology could be easily tailored. Rod-shaped ZnO arrays on the glass substrates consisted of elongated crystals having 6-fold symmetry were predominantly developed at high Zn precursor concentration in the pH range 7~11.
Abstract
The nano-array of the vertically aligned rod-like particles grown on ZnO coated glass-substrates was obtained via hydrothermal process. ZnO thin film coatings were prepared on the glass substrates using a MOD (metallorganic deposition) dip-coating method with zinc chloride dihydrate as starting material and 2-ethylhexanol as solvent. ZnO nanorods were synthesized on the seeded substrates by hydrothermal method at 80°C using zinc-nitrate hexahydrate as a Zn source and sodium hydroxide as a mineralizer. Under the hydrothermal condition, the rod-like nanocrystals were easily attaching on the already ZnO seeded (coated) glass surface. It has been shown that the hydrothermal synthesis parameters are key factors in the nucleation and growth of ZnO crystallites. By controlling of hydrothermal parameters, the ZnO particulate morphology could be easily tailored. Rod-shaped ZnO arrays on the glass substrates consisted of elongated crystals having 6-fold symmetry were predominantly developed at high Zn precursor concentration in the pH range 7~11.
참고문헌 (16)
- V. Srikant, "On the optical band gap of zinc oxide", J. Appl. Phys, 83, pp.5447~5451 (1998)
- D. C. Look, "Recent advances in ZnO materials and devices", Mater. Sci. Eng. B, 80, pp.383~387 (2001)
- A. Kołodziejczak-Radzimska, "Zinc oxide from synthesis to application : A review", Materials, 7, pp.2833~2881 (2014)
- A. Janotti, "Fundamentals of zinc oxide as a semiconductor", Rep. Prog. Phys, 72, pp.126501~126529 (2009)
- Z. L. Wang, "Zinc oxide nanostructures: growth, properties and applications", J. Phys.: Condens. Matter, 16, pp.R829~R858 (2004)
- X. Wang, "Large-scale synthesis of six-nanometer-wide ZnO nanobelts", J. Phys. Chem. B, 108, pp.8773~8777 (2004)
- S. Xu, "One-dimensional ZnO nanostructures: solution growth and functional properties", Nano Res, 4, pp.1013~1098 (2011)
- A. Pawar, "Growth of ZnO nanorods using hydrothermal for gas sensing application", Res. J. Physical Sci, 3, pp.1~3 (2015)
- Q. Zhang, "ZnO nanostructures for dye-sensitized solar cells", Adv. Mater, 21, pp.4087~4108 (2009)
- K. Nejati, "Synthesis of ZnO nanoparticles and investigation of the ionic template effect on their size and shape", Int. Nano Lett, 1, pp.75~81 (2011)
- K. Byrappa, "Handbook of Hydrothermal Technology", pp.2001, Noyes Publications
- W. L. Suchanek, "Hydrothermal synthesis of advanced ceramic powders", Adv. Sci. Tech, 45, pp.184~193 (2006)
- A. Bramantyo, "Optimization of ZnO seed layer for growth of vertically aligned ZnO nanorods on glass surface", JJAP Conf. Proc, pp.0111031~0111036 (2016)
- J. B. Wachtman, "Ceramic Films and Coating", pp.224~ (1992), Noyes Pub.
- W. Stumm, "Aquatic Chemistry", pp.1002~ (1995), Wiley-Interscience
- S. Yamabi, "Growth conditions for wurtzite zinc oxide films in aqueous solutions", J. Mater. Chem, 12, pp.3773~3778 (2002)