PEO 처리시 Ca-GP첨가에 따른 AZ31합금의 내식성 및 표면특성에 관한 연구
A study on corrosion resistance and surface properties of AZ31 alloy according to Ca-GP addition during PEO treatment
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PEO (plasma electrolytic oxidation) was applied to modify the surface of AZ31 magnesium alloy in this study. The mixed solution of sodium hydroxide (NaOH) and sodium silicate (Na2SiO3) was used as the electrolyte, and 0 – 0.05 g/L of Ca-GP (Glycerol Phosphate Calcium salt) was added in the electrolyte as an additive. PEO treatment was conducted at a current density of 30mA/cm2 for 5 minutes using a DC power supply. The surface properties were identified by SEM, XRD and surface roughness analyses, and the corrosion resistance was evaluated by potentiodynamic polarization and immersion tests. In addition, the biocompatibility was evaluated by immersion test in SBF solution. As the concentration of Ca-GP was increased, the surface morphology was denser and more uniform, and the amount of Ca and the thickness of oxide layer increased. Only Mg peak was observed in XRD analysis due to very thin oxide layer. The corrosion resistance of PEO-treated samples increased with the concentration of Ca-GP in comparision with the untreated sample. In particular, the highest corrosion resistance was identified at the group of 0.04g Ca-GP through potentiodynamic polarization and immersion tests in saline solution (0.9 wt.%NaCl). During the immersion in saline solution, pH rapidly increased at the beginning of immersion period due to rapid corrosion, and then increase rate of pH decreased. However, the pH value in the SBF temporarily increased from 7.4 to 8.5 during the day, then decreased due to the inhibition of corrosion with HA(hydroxyapatite) formation.
Abstract
PEO (plasma electrolytic oxidation) was applied to modify the surface of AZ31 magnesium alloy in this study. The mixed solution of sodium hydroxide (NaOH) and sodium silicate (Na2SiO3) was used as the electrolyte, and 0 – 0.05 g/L of Ca-GP (Glycerol Phosphate Calcium salt) was added in the electrolyte as an additive. PEO treatment was conducted at a current density of 30mA/cm2 for 5 minutes using a DC power supply. The surface properties were identified by SEM, XRD and surface roughness analyses, and the corrosion resistance was evaluated by potentiodynamic polarization and immersion tests. In addition, the biocompatibility was evaluated by immersion test in SBF solution. As the concentration of Ca-GP was increased, the surface morphology was denser and more uniform, and the amount of Ca and the thickness of oxide layer increased. Only Mg peak was observed in XRD analysis due to very thin oxide layer. The corrosion resistance of PEO-treated samples increased with the concentration of Ca-GP in comparision with the untreated sample. In particular, the highest corrosion resistance was identified at the group of 0.04g Ca-GP through potentiodynamic polarization and immersion tests in saline solution (0.9 wt.%NaCl). During the immersion in saline solution, pH rapidly increased at the beginning of immersion period due to rapid corrosion, and then increase rate of pH decreased. However, the pH value in the SBF temporarily increased from 7.4 to 8.5 during the day, then decreased due to the inhibition of corrosion with HA(hydroxyapatite) formation.
참고문헌 (20)
- Y. F. Jiang, "Corrosion protection of polypyrrole electrodeposited on AZ91 magnesium alloys in alkaline solutions", Synthetic Metals, 139, pp.335~339 (2003)
- H. Hoche, "Investigation of the macroscopic and microscopic electrochemical corrosion behaviour of PVD-coated magnesium die cast alloy AZ91", surf. Coat. Technol, 193, pp.178~184 (2005)
- Xiangyu Lu, "Investigation of the macroscopic and microscopic electrochemical corrosion behaviour of PVD-coated magnesium die cast alloy AZ91", Progress in Organic Coatings, 104, pp.188~198 (2017)
- R. Udhayan, "On the corrosion behaviour of magnesium and its alloys using electrochemical techniques", Journal of Power Sources, 63, pp.103~107 (1996)
- S-M. Moon, "마그네슘의 표면처리", pp.55~64 (2004), 한국기계연구원
- F. H Froes, "Aghion, The Science, Technology, and Applications of Magnesium", JOM, 50, pp.30~34 (1998)
- 김성종, "Sealing Effects of Anodic Oxide Films Formed on Mg-Al Alloys", Korean Journal of Chemical Engineering, 21(4), pp.915~920 (2004), 한국화학공학회
- H-I. Wu, "anodization of ZK60magnesium alloy in alkaline solution containing silicate and the corrosion properties of the anodized films", Appl. Surf. Sci, 253, pp.9387~9394 (2007)
- 정우철, "플라즈마 전해산화법에 의해 형성된 알루미늄 합금의 양극산화피막 내마모 특성에 관한 연구", 한국표면공학회지, 51(6), pp.381~386 (2018), 한국표면공학회[DOI]
- S. Durdu, "Characterization of AZ31 Mg Alloy coated by plasma electrolytic oxidation", Vacuum, 88, pp.130~133 (2013)
- 심건주, "마그네슘 합금의 플라스마전해산화 코팅에 영향을 미치는 제반 요소들에대한 고찰", 대한금속·재료학회지, 55(5), pp.296~307 (2017), 대한금속·재료학회[DOI]
- E. Ziyaei, "Corrosion Behavior of PEO Coatings Formed on AZ31 Alloy in Phosphate-Based Electrolytes with Calcium Acetate Additive", J. Mat. Eng. perform, 26, pp.3204~3215 (2017)
- M. Bobby Kannan, "Electrochemical surface engineering of magnesium metal by plasma electrolytic oxidation and calcium phosphate deposition: biocompatibility and in vitro degradation studies", RSC Advances, 8(51), pp.29189~29200 (2018)
- F. Simchen, "Composition of highly concentrated silicate electrolytes and ultrasound influencing the plasma electrolytic oxidation of magnesium", IOP Conf. Ser.: Mater. Sci. Eng., 181(012040), pp.1~13 (2017)
- 문성모, "AZ31 마그네슘 합금의 플라즈마전해산화 피막 형성에 미치는 수산화 이온 및 규산 이온의 영향", 한국표면공학회지, 47(4), pp.147~154 (2014), 한국표면공학회[DOI]
- 이종석, "AZ31 마그네슘 합금의 플라즈마 전해 산화에서 Sodium Aluminate 농도가 산화막 특성에 미치는 영향", 열처리공학회지, 25(5), pp.227~232 (2012), 한국열처리공학회
- S. Hiromoto, "Hydroxyapatite coating of AZ31 magnesium alloy by a solution treatment and its corrosion behavior in NaCl solution", Surf. Coat. Technol, 205(19), pp.4711~4719 (2011)
- 박양순, "고온 (300~1000 ℃)에서 티타늄 금속시편의 표면 산화거동", 분석과학, 22(6), pp.464~470 (2009), 한국분석과학회
- H. Chen, "Corrosion performance of plasma electrolytic oxidized AZ31magnesium alloy in silicate solutions with different additives", surf. Coat. Technol, 205, pp.532~535 (2010)
- I-S. Park, "Biomimetic apatite formation and biocompatibility on chemically treated Ti-6Al-7Nb alloy", Surf. Interface. Anal, 40, pp.37~42 (2008)