발전소 절탄기 튜브의 배기가스 온도와 황산 농도에 따른 노점 및 내식성 분석
Analysis of dew point and corrosion resistance for power plant economizer tube with exhaust gas temperature and sulfuric acid concentration
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Environmental pollution caused by power plant exhaust gas is highlighted and eco-friendly regulations are being strengthened. However, due to the abundant reserves and low prices of coal, still the most used for power generation in the world. Therefore, flexible operation of coal-fired power plants to reduce emissions has become an inevitable option. However, lowering the output increases the possibility of acid dew point corrosion as the exhaust gas temperature decreases. The dew point corrosion occurs when condensable gases such as SO3, HCl, NO2 and H2O cools below the saturation temperature. SO3 is already well known to cause severe low- temperature corrosion in coal-fired power plants. Therefore, this study aims to prevent damage that may occur during operation by analyzing the dew point and corrosion resistance with exhaust gas temperature and sulfuric acid concentration of the power plant economizer tube.
Abstract
Environmental pollution caused by power plant exhaust gas is highlighted and eco-friendly regulations are being strengthened. However, due to the abundant reserves and low prices of coal, still the most used for power generation in the world. Therefore, flexible operation of coal-fired power plants to reduce emissions has become an inevitable option. However, lowering the output increases the possibility of acid dew point corrosion as the exhaust gas temperature decreases. The dew point corrosion occurs when condensable gases such as SO3, HCl, NO2 and H2O cools below the saturation temperature. SO3 is already well known to cause severe low- temperature corrosion in coal-fired power plants. Therefore, this study aims to prevent damage that may occur during operation by analyzing the dew point and corrosion resistance with exhaust gas temperature and sulfuric acid concentration of the power plant economizer tube.
참고문헌 (20)
- A centurial history of technological change and learning curves for pulverized coal-fired utility boilers, "Y. Sonia", Energy, 1996~2005 (2007)
- A global coal production forecast with multi-Hubert cycle analysis, "W. P. Tadeusz", Energy, 3109~3122 (2010)
- J. Ahn, "Sulfur trioxide formation during oxy-coal combustion", Int. J. Greenh. Gas Control, pp.127~135 (2011)
- Y. Tan, "Combustion characteristics of coal in a mixture of oxygen and recycled flue gas", Fuel, pp.507~512 (2006)
- R. Stanger, "Sulphur impacts during pulverised coal combustion in oxy-fuel technology for carbon capture and storage", Prog. Energy Combust. Sci, pp.69~88 (2011)
- D. Fleig, "SO3 formation under oxyfuel combustion conditions", Ind. Eng. Chem. Res, pp.8505~8514 (2011)
- V. Lins, "Failure of a heat exchanger generated by an excess of SO2and H2S in the sulfur recovery unit of a petroleum refinery", J. Loss Prevent Proc. Ind, pp.91~97 (2007)
- W. M. M. Huijbregts, "Latest advances in the understanding of acid dew point corrosion: corrosion and stress corrosion cracking in combustion gas condensates", Anti-Corros. Method Mater, pp.173~188 (2004)
- U. Anees, "Studies on the Failure of Economizer Tubes Involving Acid Dew-Point Corrosion in High Pressure Boilers", International Journal of Scientific &Engineering Research, pp.1726~1736 (2013)
- P. D. Moskovits, "Low-temperature boiler corrosion and deposits - A literature review", Ind. Eng. Chem., pp.1305~1312 (1959)
- Y. Takizawa, "Corrosionresistant Ni-Cr-Mo alloys in hot concentrated sulphuric acid with active carbon", Mater. Sci. Eng. A, 198, pp.145~152 (1995)
- A. Bahadori, "Estimation of combustion flue gas acid dew point during heat recovery and efficiency gain", Applied Thermal Engineering, 31, pp.1457~1462 (2011)
- M. B. Rockel, "Corrosion Handbook, Society for Chemical Engineering and Biotechnology" (2008), Germany
- M. A. Quraishi, "Inhibition of mild steel corrosion in sulfuric acid solution by thiadiazoles", J. Appl. Electrochem, pp.539~544 (2006)
- M. Cherif, "Representation of VLE and liquid phase composition with an electrolyte model", Fluid Phase Equilib, pp.729~738 (2002)
- S. Ciukaj, "Dew point of the flue gas of boilers co-firing biomass with coal", Chem Process Eng-Inz (2013)
- 박선아, "황산·염산 복합 내식강 개발: 2. 현장 적용성 평가를 통한 개발강의 신뢰성 검증", 대한금속·재료학회지, 52(11), pp.857~872 (2014), 대한금속·재료학회[DOI]
- L. Dahl, "Corrosion in flue gas desulfurization plants and other low temperature equipment", Werkstoffe und Korrosion, pp.298~304 (1992)
- Y. G. Wang, "Mechanism research on coupling effect between dew point corrosion and ash deposition", Applied Thermal Engineering, pp.102~110 (2013)
- D. Lampert, "Low-temperature corrosion in feed-heaters heated by flue gas", Brown Boveri Rev, pp.691~695 (1978)