DTP 반응성 잉크용 저점도 아크릴계 고분자 전처리액 제조 및 특성 평가
Preparation and Evaluation of Low Viscosity Acrylic Polymer Based Pretreatment Solution for DTP Reactive Ink
2
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
In the direct digital textile printing process, the pre-treatment process is an essential condition for products by forming a clear pattern by sticking and penetration of DTP dye without spreading on the fabric. Recently, pre-treatment agent is changing from high viscosity to low viscosity in order to reduce defects of fabric during pre-treatment process. In this study, pre-treatment agent of acrylic polymer with low viscosity(less than 50cps) was prepared according to the solid content of the polymer, pre-treated on the cotton fabric, and Direct DTP printing was performed to compare the color and sharpness. As a result, it showed high color at a viscosity of 50cps or less. When the solid content of the polyacrylic acid having a high molecular weight(A1) was 2.5wt%, when the solid content of the polyacrylic acid having a low molecular weight(A2) was 1 - 1.5wt%, the color was the best. And when the solid content of A1 and A2 was 1.5wt%, the degree of spreading was small and A1 was superior to A2 at the sharpness.
Abstract
In the direct digital textile printing process, the pre-treatment process is an essential condition for products by forming a clear pattern by sticking and penetration of DTP dye without spreading on the fabric. Recently, pre-treatment agent is changing from high viscosity to low viscosity in order to reduce defects of fabric during pre-treatment process. In this study, pre-treatment agent of acrylic polymer with low viscosity(less than 50cps) was prepared according to the solid content of the polymer, pre-treated on the cotton fabric, and Direct DTP printing was performed to compare the color and sharpness. As a result, it showed high color at a viscosity of 50cps or less. When the solid content of the polyacrylic acid having a high molecular weight(A1) was 2.5wt%, when the solid content of the polyacrylic acid having a low molecular weight(A2) was 1 - 1.5wt%, the color was the best. And when the solid content of A1 and A2 was 1.5wt%, the degree of spreading was small and A1 was superior to A2 at the sharpness.
참고문헌 (14)
- 정용순, "디지털 텍스타일 프린팅과 재래식 스크린 날염의 비교연구", 디자인학연구, 17(2), pp.49~ (2004), 한국디자인학회
- 박순영, "DTP(Digital Textile Printing)에서 미디어의 원사꼬임 및 편성구조가 프린팅 Quality에 미치는 영향(I)", 한국염색가공학회지, 22(3), pp.282~291 (2010), 한국염색가공학회
- 이산하, "견직물의 디지털 프린팅에 있어 전처리제가 염색성에 미치는 영향", 한국염색가공학회지, 23(4), pp.263~273 (2011), 한국염색가공학회
- 엄경희, "디지털 전사 프린팅 활용성 고찰- 전폭 민화벽지디자인을 중심으로 -", 한국디자인문화학회지, 11(4), pp.118~126 (2005), 한국디자인문화학회
- 조문희, "승화전사 디지털 텍스타일 프린트의 전사 조건에 관한 연구", 한국패션디자인학회지, 10(4), pp.59~67 (2010), 한국패션디자인학회
- 기샛별, "카라기난(Carrageenan)의 셀룰로오스 직물 DTP 전처리호제로써의 가능성 연구", 한국염색가공학회지, 27(4), pp.318~326 (2015), 한국염색가공학회
- 홍민기, "고발색 디지털 프린팅을 위한 미디어 전처리 기술", 한국염색가공학회지, 19(4), pp.1~9 (2007), 한국염색가공학회
- 박순영, "DTP(Digital Textile Printing)용 후처리 및 연속공정 시스템에 관한 연구", 패션 비즈니스, 15(5), pp.43~54 (2011), 한국패션비즈니스학회
- 김은지, "비닐트리에톡시실란으로 개질된 폴리비닐알코올", 폴리아크릴산 필름의 내수성 및 차단성 연구, 2012, pp.18(1), 57~62[DOI]
- 정동석, "디지털 프린팅 견직물의 색상 변화 및 견뢰도- 혼합 전처리제의 영향", 한국의류산업학회지, 15(5), pp.808~814 (2013), 한국의류산업학회
- 이연순, "섬유 종류에 따른 디지털 텍스타일 프린팅의 발색성 비교 분석", 한국의상디자인학회지, 12(2), pp.67~73 (2010), 한국의상디자인학회
- 황소희, "견직물의 소목염색에서 단백질 전처리 효과", 한국염색가공학회지, 28(3), pp.208~218 (2016), 한국염색가공학회