유물 복원을 위한 천연 셀룰로오스 직물의 산에 의한 열화 특성 연구
A Study on the Acid Degradation Properties of Cellulose Fabrics for Costume Heritage Restoration
0
조회
0
다운로드
1
인용
0
참고문헌
초록
Abstract
to preserve and restore the excavated cellulose fabrics as costume heritages have been carried out. In this study, in order to artificially restore an excavated cellulose fabrics, acid-treated cellulose fabrics were prepared. Three kinds of cellulose fabrics were used for an experiment. Three kinds of cellulose fabrics were treated by the acid aqueous solution for the various strength retention (100%, 80%, 60%, 40%, 20%). The fine structure and physical properties of acid treated cellulose fabrics were investigated with various techniques such as wide-angle X-ray diffraction, tensile test, weight loss, shrinkage, SEM etc. Tensile strength and strain of cellulose fabrics decreased with increasing acid treatment time. However, weight loss and shrinkage increasing slightly. The crystal diffraction intensity was not changed. SEM results of acid-treated cellulose fabrics show that the surface was damaged.
참고문헌 (10)
- "문화재의 과학적 보존", pp.110~118 (1994)
- "Degradation Measurements of Linen Fabrics", 43(5), pp.1377~1386 (2004)
- "Analysis of Buried-Fabrics from the Tomb-Kim Hum Jo by Physical J. of the Korean Society of Clothing and Textiles", pp.809~819 (1999)
- "Chemical principles of Textile Conservation", pp.28~29 (1998), Butterworth-Heinemann
- "United States of America", pp.41~ (1995), Prentice Hall Inc.
- "The Effects of Various Pulping Conditions on Crystalline Structure of Cellulose in Cotton Linters", 81, pp.559~564 (2003)
- "Mercerization of Cellulose Ⅲ-Changes in Crystallite sizes-", 33, pp.855~866 (1987)
- "Evaluation of Turkish Cotton Versus its Maturity Degree", pp.86~89 (1996)
- "Structure Differences between Non-wood Plant Cellulose Evidence from Solid State NMR", pp.245~249 (2002)
- "A Study on Structure and Properties of Cellulose, Wool, and Nylon 6 Fibers Treated with Liquid ammonia", thesis (2002), Pusan National University