Wool 직물의 나노 발수 발유가공
Water and Oil Repellency of Wool Fabric Treated with Nano-type Finishing Agent
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
Wool fabric having high moisture content were treated with fluorocarbon-based water and oil repellent finishing agents by pad-dry-cure system. Three types of finishing agents which were regular-type or nano-type were adapted to compare the surface chemical composition, water and oil repellent property, crease recovery angle, and durability to repeated laundering. From the surface chemical compositions resulted by ESCA and C1s curve-fitting, it was shown that the regular-type finishing agent were easily taken off from the finished wool fabrics after repeated laundering. On the other hand, the fluoroalkyl groups of nano-type finishing agents turned round from fabric surface to fiber internal after repeated laundering. The water repellency of the wool fabrics treated with regular-type agent had a little changes according to the treatment condition changes and sharply decreased with repeated laundering. However, these values when treated with nano-type agents increased with the concentration and cure temperature and were maintained after 20 times laundering. The wool fabrics treated with nano-type agent had a great oil repellency irrespective of treatment conditions. Furthermore, the wrinkle recovery values of the wool fabrics treated with nano-type agents were higher than those of the fabrics treated with regular-type agent and were unchanged after 20 times laundering.
Abstract
Wool fabric having high moisture content were treated with fluorocarbon-based water and oil repellent finishing agents by pad-dry-cure system. Three types of finishing agents which were regular-type or nano-type were adapted to compare the surface chemical composition, water and oil repellent property, crease recovery angle, and durability to repeated laundering. From the surface chemical compositions resulted by ESCA and C1s curve-fitting, it was shown that the regular-type finishing agent were easily taken off from the finished wool fabrics after repeated laundering. On the other hand, the fluoroalkyl groups of nano-type finishing agents turned round from fabric surface to fiber internal after repeated laundering. The water repellency of the wool fabrics treated with regular-type agent had a little changes according to the treatment condition changes and sharply decreased with repeated laundering. However, these values when treated with nano-type agents increased with the concentration and cure temperature and were maintained after 20 times laundering. The wool fabrics treated with nano-type agent had a great oil repellency irrespective of treatment conditions. Furthermore, the wrinkle recovery values of the wool fabrics treated with nano-type agents were higher than those of the fabrics treated with regular-type agent and were unchanged after 20 times laundering.
참고문헌 (9)
- 東レ, "日本特許開昭 56-144200", ~ (1983)
- 改森 道改, "ウール加工", 新商品․新技術開發のキー技術, 2004, pp.통권 : 39, 534~539
- 東海染工, "ナノテクノロジーを用いた纖維加工商品", Textile Processing Technology (Japan), 통권 : 40, pp.12~13 (2005)
- D. C. Rha, "Durable Water and Oil Repellent Finish of Wool Fabric(I)", J. Korean Soc. Dyers & Finishers, 통권 : 10, pp.33~37 (1998)
- B. O. Lee, "Water Repellent Finish for Divided Type PET", Nylon Fabrics with Fluoro Alkyl Resin, 1997, pp.9(4), 213~218
- T. Wakida, "Effect of Washing and Subsequent Heat Treatment on the Water Repellency of Poly(ethylene terephthalate) Fabric and Film treated 최보련․한삼숙․이문철 Ⅰ34Ⅰ한국염색가공학회지 제 20권 제 6호 with Carbon Tetrafluoride and trifluoromethane Low-Temperature Plasmas", Sen'i Gakkaishi, 통권 : 50, pp.533~537 (1994)
- T. Wakida, "The Effect of Washing and Heat Treatment on the Surface Characteristics of Fluorocarbon Resin-treated Polyester", J. Soc. Dyers Colour, 통권 : 109, pp.292~296 (1993)
- T. Wakida, "A Change of Surface Characteristics of Commercial Water Repellent Fabrics by Washing and Subsequent Ironing", Jpn. Res. Assn. Text. End-Uses, 통권 : 42, pp.113~119 (2001)
- J. Koga, "Principle and Problem in Functional Finishing of Wool", J. Korean Soc. Dyers & Finishers, 통권 : 3, pp.247~252 (1991)