자외선/오존 조사에 의한 Poly(vinyl butyral)의 광산화
Photooxidation of Poly(vinyl butyral) Films by UV/Ozone Irradiation
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Poly(vinyl butyral), PVB, was photooxidized by UV/ozone irradiation and the effect of UV energy on the surface properties of the UV-irradiated PVB film were investigated by the measurement of reflectance, surface roughness, contact angles, elemental composition, and zeta potential. With increasing UV energy, reflectance decreased in the visible and ultraviolet regions particularly at the wavelength of 400nm. The irradiation produced nano-scale surface roughness including the maximum peak-to-valley roughness increased from 274nm for the unirradiated PVB to 370nm at the UV energy of 5.3J/cm². The improved hydrophilicity was due to the higher O1s/C1s resulting from the introduction of polar groups such as C=O bonds. The surface energy of the PVB film increased from 35.3mJ/m² to 39.3mJ/m² at the irradiation of 15.9J/cm². While the zeta potentials decreased proportionally with increasing UV energy, the cationic dyeability of the PVB increased accordingly resulting from the improved affinity of the irradiated PVB surfaces containing the photochemically introduced anionic and dipolar dyeing sites.
Abstract
Poly(vinyl butyral), PVB, was photooxidized by UV/ozone irradiation and the effect of UV energy on the surface properties of the UV-irradiated PVB film were investigated by the measurement of reflectance, surface roughness, contact angles, elemental composition, and zeta potential. With increasing UV energy, reflectance decreased in the visible and ultraviolet regions particularly at the wavelength of 400nm. The irradiation produced nano-scale surface roughness including the maximum peak-to-valley roughness increased from 274nm for the unirradiated PVB to 370nm at the UV energy of 5.3J/cm². The improved hydrophilicity was due to the higher O1s/C1s resulting from the introduction of polar groups such as C=O bonds. The surface energy of the PVB film increased from 35.3mJ/m² to 39.3mJ/m² at the irradiation of 15.9J/cm². While the zeta potentials decreased proportionally with increasing UV energy, the cationic dyeability of the PVB increased accordingly resulting from the improved affinity of the irradiated PVB surfaces containing the photochemically introduced anionic and dipolar dyeing sites.
참고문헌 (19)
- E. S. Wilks, "Industrial Polymers Handbook", pp.963~967 (2001), Wiley-VCH
- J. E. Mark, "Polymer Data Handbook", pp.910~924 (1999), Oxford University Press
- 서광원, "침전법에 의한 폴리비닐부티랄의 제조 및 특성분석", 폴리머, 26(2), pp.168~173 (2002), 한국고분자학회
- X. Fu, "Structure Control of Asymmetric Poly(vinyl butyral)-TiO2Composite Membrane Prepared by Nonsolvent Induced Phase Separation", J. Appl. Polym. Sci, 108, pp.713~ (2008)
- X. Ma, "Antifouling Property Improvement of Poly(vinyl butyral) Ultrafiltration Membranes through Acid Treatment", Separation and Purification Technology, 54, pp.220~ (2007)
- S. H. Lee, "The Analysis on PVB Film Optical Characteristics for PV Module Generating in High Temperature", The Korean Institute of Electrical Engineers, 7, pp.20~ (2011)
- F. Lian, "A Novel PVB based Polymer Membrane and its Application in Gel Polymer Electrolytes for Lithium-ion Batteries", J. Membrane Science, 456, pp.42~ (2014)
- Y. Dong, "The Enhanced Cationic Dyeability of Ultraviolet", Ozone-treated meta-Aramid Fabrics, 2011, pp.127, 173~
- 윤득원, "Surface Modification of Ultra High Molecular Weight Polyethylene Films by UV", ozone Ir radiation, 2011, pp.23(2), 76~82[DOI]
- 장용준, "UV", Ozone 조사에 의한 Poly(phenylene sulfide) 필름의 표면처리과 염색성, 2011, pp.23(4), 284~289[DOI]
- 김민수, "자외선", 오존 조사에 의한 Poly Ketone의 광산화와 염색성, 2013, pp.25(1), 25~29[DOI]
- 주진우, "자외선", 오존 조사에 의한 Poly(butylene succinate) 필름의 광산화, 2014, pp.26(3), 159~164[DOI]
- G. H. Koo, "Depth-Gradient and Photoinitiator-free Photocrosslinking of Poly (ethylene oxide)", J. Appl. Polym. Sci, 125, pp.2659~ (2012)
- 장용준, "아세토페논을 함유한 Poly(phenylene sulfide)의 광가교에 의한 내열성과 인장인성 강화", 한국염색가공학회지, 24(4), pp.281~287 (2012), 한국염색가공학회
- G. H. Koo, "Preparation of Melting-Free Poly(lactic acid) by Amorphous and Crystal Crosslinking under UV Irradiation", J. Appl. Polym. Sci, 127, pp.4515~ (2013)
- D. W. Yun, "Wear Minimization of Ultra High Molecular Weight Polyethylene by Benzophenone-assisted Photocrosslinking", Fibers and Polymers, 15(3), pp.480~ (2014)
- D. W. Yun, "Acetophenone-Assisted Main-Chain Photocrosslinking of Poly(ethylene terephthalate)", J. Appl. Polym. Sci, 131, pp.3980~ (2014)
- R. Shishoo, "Plasma Technology for Textiles", pp.1~24 (2007), Woodhead Publishing
- 진성우, "TiO2 광촉매를 함유한 PET와 나일론 6 나노복합체막의 자외선", 오존에 대한 안정성, 2014, pp.26(2), 88~98[DOI]