The Effect of Annealing Heat Treatment by Anodic Polarization Impedance Experiments for Cu-10%Ni Alloy
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Copper has been used extensively as an electric wire or as a base material in various types of machineries owing to its good electrical and thermal conductivity and good fabricating property, as well as its good corrosion resistance compared to iron. Furthermore, the copper-nickel alloy has significant corrosion resistance in severely corrosive environments. Although, cupro-nickel alloy shows better corrosion resistance than the brass and bronze series, this alloy also corroded in severely corrosive environments, including aggressive chloride ions, dissolved oxygen, and condition of fast flowing seawater. In this study, and annealing treatment at various annealing temperatures was carried out on the cupro-nickel (Cu-10%Ni) alloy, and the effects of annealing were investigated using electrochemical methods, such as measuring the polarization and impedance behaviors under flowing seawater conditions. The corrosion resistance increased by annealing compared to non heat treatment in the absence of flowing seawater. In particular, the sample annealed at 200 ℃ exhibited the best corrosion resistance. The impedance in the presence of flowing seawater showed higher values than in the absence of flowing seawater. Furthermore, the highest impedances was observed in the sample annealed at 800 ℃, irrespective of the present of flowing seawater. Consequently, the corrosion resistance of cupro-nickel (Cu-10%Ni) alloy in a severely corrosive environment can be improved somewhat by annealing.
Abstract
Copper has been used extensively as an electric wire or as a base material in various types of machineries owing to its good electrical and thermal conductivity and good fabricating property, as well as its good corrosion resistance compared to iron. Furthermore, the copper-nickel alloy has significant corrosion resistance in severely corrosive environments. Although, cupro-nickel alloy shows better corrosion resistance than the brass and bronze series, this alloy also corroded in severely corrosive environments, including aggressive chloride ions, dissolved oxygen, and condition of fast flowing seawater. In this study, and annealing treatment at various annealing temperatures was carried out on the cupro-nickel (Cu-10%Ni) alloy, and the effects of annealing were investigated using electrochemical methods, such as measuring the polarization and impedance behaviors under flowing seawater conditions. The corrosion resistance increased by annealing compared to non heat treatment in the absence of flowing seawater. In particular, the sample annealed at 200 ℃ exhibited the best corrosion resistance. The impedance in the presence of flowing seawater showed higher values than in the absence of flowing seawater. Furthermore, the highest impedances was observed in the sample annealed at 800 ℃, irrespective of the present of flowing seawater. Consequently, the corrosion resistance of cupro-nickel (Cu-10%Ni) alloy in a severely corrosive environment can be improved somewhat by annealing.
참고문헌 (12)
- D . P. Cox, "Copper resources in ency clopedia of materials science and engineering", pp.855~859 (1986), Dergamon Press and the MIT Press
- T. Cunningham, "Marine coating inspection program" (1997), NACE International Houston
- The Marine Enviroment, "T. Cunningham", NACE International Houston, ~, pp.Version 97-1 (1997)
- Cathelco, "Antifouling System Operation Manual", ~ (1976)
- Marine Fouling and Its Prevention, "U. S. Naval Institute" (1952), Annapolis, Md
- H. C. Flemming, "Biofouling and biocorrosion in industrial water system", Proceedings of International Workshop on Industrial Biofouling and Biocorrosion, pp.13~14 (1990)
- "Standard Method for Testing Antifouling Panels in Shllow Submergence", ASTM, ~ (1993)
- R. W. Cahn, "A comprehensive treatment, structure and properties of nonferrous alloys", Materials Science and Technology, 8, pp.234~ (1996)
- E. G. West, "Copper and Its Alloys", pp.567~ (1982), Ellis Horwood Ltd., Halsted Press
- Marine Engineering Practice:Selecting Materials for Seawater Systems, "B. Todd", Institute of Marine Engineers, 789~, pp.Technical Report 7 (1976)
- 문경만, "몰타르 시험편(W", C:0.4) 내부철근의 분극특성에 미치는 재령년수의 영향, 2014, pp.13(1), 20~27[DOI]
- K. M. Moon, "Practical Electrochemistry", pp.187~ (1999), Edited by Hyou Sung Co. Ltd