재활용 폐자원에 따른 지오폴리머의 특성변화 연구
Characteristics of geopolymer based on recycling resources
0
조회
0
다운로드
10
인용
0
참고문헌
초록
본 연구는 알칼리 활성화제로 NaOH와 물유리를 사용하고 리젝트애쉬와 고로슬래그를 혼합하여 지오폴리머를제조하였다. 리젝트애쉬와 고로슬래그의 치환율과 물유리와 NaOH의 농도에 따른 압축강도를 측정하였다. 압축강도 측정결과로는 알칼리 활성화제로 NaOH 1 wt%, 물유리 3 wt%와 전량 고로슬래그를 사용한 경우 재령 28일차 강도가 38.91MPa의 성능을 나타내었다. 압축강도 증진의 중요한 요인은 알칼리 활성화제의 비율과 리젝트애쉬와 고로슬래그의 치환율에 의한 것이었다.
Abstract
In this study, geopolymer was prepared with reject ash and blast furnace slag using NaOH as an alkali activator and water glass. The aim of this study was to investigate the compressive strength variation according to the contents of NaOH and water glass and replacement ratio of reject ash (RA) and blast furnace slag (BS). The compressive strength measured after 28 days was 38.91 MPa for the geopolymer which consist of 100 % of BS with 1 wt% NaOH and 3 wt%water glass. The major factor for improving compressive strength was the alkali activator proportion and the replacement ratio of RA and BS.
참고문헌 (15)
- UNEP, "Kyoto protocol", pp.12~ (2002), UNEP Press
- Q. Zhao, "Novel geopolymer based composites with enhanced ductility", J. Mater. Sci, 42, pp.3131~ (2007)
- K. Komnitas, "Geopolymerrisation; A review and prospects for the minerals industry", Miner. Eng, 20, pp.1261~ (2007)
- L. Provis, "Correlating mechanical and thermal properties of sodium silicate-fly ash geopolymer", J. Mater. Sci, 336, pp.57~ (2009)
- D. Panias, "Effect of synthesis parameters on the mechanical properties of fly ash-based geopolymers", Colloid Surf. A-physicochem. Eng. Asp, 301, pp.246~ (2007)
- J.L. Bell, "Formation of ceramics from metakaolin-based geopolymers: Part 1-CS-based geopolymer", J. Am. Ceram. Soc, 92, pp.1~ (2008)
- J. Davidovits, "Geopolymers and geopolymeric materials", J. Therm. Anal, 35, pp.429~ (1989)
- J. Davidovits, "Inorganic polymeric new materials", J. Them. Anal, 37, pp.1633~ (1991)
- 이우근, "소각재를 이용한 무기결합제의 제조 및 특성", 한국폐기물자원순환학회지, 25(1), pp.9~14 (2008), 한국폐기물자원순환학회
- Z. Yunsheng, "Synthesis and heavy metal immobilization behaviors of slag based geopolymer", J. Hazard. Mater, 143, pp.206~ (2006)
- Sindhunata, "A conceptual model of geopolymerisation, PhD thesis", 박사, pp.2006
- P. Duxson, "The role of inorganic polymer technology in the development of ‘'Green concrete’'", Cem. Concr. Res, 37, pp.1590~ (2007)
- L. Choi, "Solving direction of the environmetal friendly policy in Korea cement industy", Magazine of the Korea Concrete Institute, 18, pp.8~ (2006)
- 이강필, "고분말 리젝트애시를 혼입한 시멘트복합체의 기본물성에 관한 연구", 한국건축시공학회지, 11(4), pp.363~370 (2011), 한국건축시공학회
- 김유택, "화력발전소 잔사회 입도에 따른 에코인공골재의 특성에 관한 연구", 한국결정성장학회지, 20(4), pp.185~191 (2010), 한국결정성장학회