나노 분말을 Spark Plasma 소결해 제조한 PbTe의 열전 특성
Thermoelectric Properties of PbTe Prepared by Spark Plasma Sintering of Nano Powders
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Nanoparticles of PbTe are prepared via chemical reaction of the equimolar aqueous solutions of Pb(CH3COO)2 and Te at 120°C. The size of the obtained particles is 100 nm after calcination in a hydrogen atmosphere. Dense specimens for the thermoelectric characterization are produced by spark plasma sintering of prepared powders at 400°C to 500°C under 80 MPa for 5 min. The relative densities of the prepared specimens reach approximately 97% and are identified as cubic based on X-ray diffraction analyses. The thermoelectric properties are evaluated between 100°C and 300°C via electrical conductivity, Seebeck coefficient, and thermal conductivity. Compared with PbTe ingot, the reduction of the thermal conductivities by more than 30% is verified via phonon scattering at the grain boundaries, which thus contributes to the increase in the figure of merit.
Abstract
Nanoparticles of PbTe are prepared via chemical reaction of the equimolar aqueous solutions of Pb(CH3COO)2 and Te at 120°C. The size of the obtained particles is 100 nm after calcination in a hydrogen atmosphere. Dense specimens for the thermoelectric characterization are produced by spark plasma sintering of prepared powders at 400°C to 500°C under 80 MPa for 5 min. The relative densities of the prepared specimens reach approximately 97% and are identified as cubic based on X-ray diffraction analyses. The thermoelectric properties are evaluated between 100°C and 300°C via electrical conductivity, Seebeck coefficient, and thermal conductivity. Compared with PbTe ingot, the reduction of the thermal conductivities by more than 30% is verified via phonon scattering at the grain boundaries, which thus contributes to the increase in the figure of merit.
참고문헌 (14)
- H. B. Callen, "Thermodynamics and an Introduction to Thermostatics" (1985), Wiley
- Z. Dughaish, , Physica B, 322, pp.205~ (2002)
- L. D. Hicks, , Phys. Rev. B, 47, pp.16631~ (1993)
- H. J. Goldsmid, "Recent Trends in Thermoelectric Materials Research I, Vol. 69", pp.1~5 (1964), Academic Press
- G. S. Nolas, "Thermoelectrics", pp.2~5 (2001), Springer-Verlag
- T. C. Harman, , Science, 297, pp.2229~ (2002)
- K. F. Hsu, , Science, 303, pp.818~ (2004)
- J. H. Chae, , J. Alloy. Compd., 413, pp.259~ (2006)
- G. Nimtz, "Narrow-Gap Lead Salts" (1983), Springer
- R. Allgaier, , Phys. Rev., 111, pp.1029~ (1958)
- Y. Q. Cao, , J. Phys. D: Appl. Phys., 42, pp.015406~ (2009)
- M. S Dresselhaus, , Semiconduct. Semimet., 71, pp.1~ (2001)
- R. Venkatasubramanian, , Semiconduct. Semimet., 71, pp.175~ (2001)
- C. H. Kuo, , J. Electron. Mater, 38, pp.1956~ (2009)